 PUR based single component, paste-type, reactive adhesive which hardens very quickly in the presence of moisture. Cures to give maximum and temperature resistance.
- Hardens in the presence of moisture, therefore, wood containing a moisture of up to 25% can be glued using this adhesive
- As a consequence of it's paste-type composition the adhesive does not run out of verical joints
- Able to fill the joint because the adhesive expands during the hardening process
- Resistant to water, dilute acids, dilute alkalis and solvents
- D4 in accordance with DIN EN 204
- Temperature resistant from -30°C to + 100°C
Directions for Use
- At least one of the materials in contact with the adhesive must contain the moisture which is absolutely essential for hardening
- The surface must be clean and free from grease
- Roughen non-porous material e.g. rubber
- A good fit is very important for a high final bond strength
- The right to make changes is reserved
- We always recommend doing your own test pieces
Areas of Application
For temperature and water resistant adhesive joints between pieces of wood and bonds between combinations of wood, rubber, concrete, polystyrene and polyurethane foam and cork, plus combinations of metal and a porous base material.
Technical Data
Base Raw Material |
Polyurethane |
Specific Weight |
1.13kg |
Solid Content |
Approx. 100% |
Hardening Speed |
See graph below |
Time taken to form a skin |
Approx. 10 minutes |
Ability to withstand full load |
Approx. 8 hours |
Shear Strength |
Approx. 90kg / cm² |
Shelf Life |
6 months |
Bond time to the touch |
10-20 minutes |
|